CEM II/B-M (V-LL) 32.5 R
Multicomponent Portland cement
Composition
- Portland clinker in the amount of 65-79%
- Fly ash silica and limestone in a total amount of 21-35%
- Calcium sulfate as a setting time regulator
Characteristics
- Specific gravity 2.93 kg/dm3
- Volume of 100 kg of cement is 34.1 dm3
- Bulk density 1.35 t/m3
- Moderate strength development dynamics
- Moderate heat of hydration
- Good workability and plasticity of concrete mix
- Optimal time to maintain the working properties of the concrete mix
- Very good adhesion to the substrate (significant reduction in the need to use hydrated lime for the production of mortar and plaster - cost reduction of mortar production)
- Low shrinkage
Application
- Ordinary concrete, commercial according to PN-EN 206-1
- Cement and cement-lime building mortars: "masonry and plastering"
- Concrete for large and small prefabricated products
- "Lean" concrete for substructures of load-bearing structures
Meets requirements
- PN-EN 197-1 standards "Cement - Part 1: Composition, requirements and conformity criteria for common cements"
- PN-EN 197-2 standards "Cement - Part 2: Assessment and verification of constancy of performance"
| REQUIREMENTS according to EN 197-1 | UNIT | REQUIRED VALUES |
| Compressive strength after 2 days | MPa | ">= 10.0" |
| Compressive strength after 28 days | MPa | ">= 32.5 <= 52.5" |
| Setting time (beginning) | min | ">= 75" |
| Volume stability | mm | "<= 10" |
| Sulfate content (as SO3) | % | "<= 3.5" |
| Chloride content | % | "<= 0.10" |
| Chromium content Cr(VI) | ppm | "<= 2.0" |